发光学报, 2018, 39 (10): 1451, 网络出版: 2018-11-25   

喷墨打印和旋涂法制备有机电致发光显示器件中空穴注入及发光层的比较研究

Comparing of Inkjet Printing Versus Spin Coating for Preparing Fine Structure Hole Transfer and Emitting Layers in OLED Display Construction
作者单位
1 中国科学院 苏州纳米技术与纳米仿生研究所, 江苏 苏州 215123
2 中国科学院大学, 北京 100049
摘要
比较了喷墨印刷和旋涂PEDOT∶PSS薄膜的表面性能, 发现喷涂PEDOT∶PSS薄膜上印有发射层油墨后, 其表面性能有很大差异。在喷墨打印PEDOT∶PSS膜的表面上只发现了大量的和类山状的聚合物颗粒。 进一步的研究表明, 形态的差异源于润湿性的不同。揭示了喷墨打印和旋涂对膜性能的不同影响, 从而在喷墨打印PEDOT∶PSS膜上构建了更精细的结构。
Abstract
A comparison between the surface properties of inkjet printed and spin coated PEDOT∶PSS films was made in consequence of the intriguing distinction after printing emitting layer inks on them. The sizable and hill-like polymer grains were only found on the surface of the inkjet printed PEDOT∶PSS film. Further investigation demonstrated the difference in morphology stems from the diverse of wetting properties. The differing effects on film properties between inkjet printing and spin coating were revealed, according to which a finer structure was constructed on inkjet printed PEDOT∶PSS film.

陈文斌, 郭文瑞, 牟婉莹, 杜真真, 唐鹏宇, 苏文明, 张东煜. 喷墨打印和旋涂法制备有机电致发光显示器件中空穴注入及发光层的比较研究[J]. 发光学报, 2018, 39(10): 1451. CHEN Wen-bin, GUO Wen-rui, MOU Wan-ying, DU Zhen-zhen, TANG Peng-yu, SU Wen-ming, ZHANG Dong-yu. Comparing of Inkjet Printing Versus Spin Coating for Preparing Fine Structure Hole Transfer and Emitting Layers in OLED Display Construction[J]. Chinese Journal of Luminescence, 2018, 39(10): 1451.

本文已被 4 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!