聚碳酸酯红外激光抛光工艺的研究

Study on Infrared Laser Polishing Process of Polycarbonate
作者单位
华南师范大学广东省微纳光子功能材料与器件重点实验室, 广东 广州510006
摘要
利用激光作用的一维热传导模型进行数值计算, 在确定聚碳酸酯(PC)表面抛光所需要的功率密度为104 W/cm2数量级的条件下, 比较了不同的激光扫描速度对聚碳酸酯表面抛光效果的影响。结果表明, 最优抛光参数为:离焦量正5 cm, 峰值功率密度3.1×104 w/cm2, 扫描速度20 mm/s, 此时可以将PC样品的表面粗糙度由5 μm降至2 μm, 而不会使样品变质。随着激光扫描次数的增加, 样品的表面粗糙度进一步下降, 并在扫描10次左右达到最小值。这一结果对降低PC表面的粗糙度具有指导意义。
Abstract
The numeral calculations of laser action was carried out by using one-dimensional heat conduction model. Different polishing effect on polycarbonate surface with different values of scanning speed were compared on the condition that the range of the laser power density for polycarbonate polishing was in the order of 104 W/cm2. The results show that the optimal processing parameters are as follows: the defocusing amount is 5 cm, the peak power density is 3.1×104 w/cm2, and the scanning speed is 20 mm/s, and the surface roughness of the PC sample can decrease from 5 μm to 2 μm without deterioration. With the increasing of the times of laser scanning, the surface roughness of the sample further decreased, and reached the minimum value around 10 times. The study is helpful for reducing the roughness of the PC surface.

徐思志, 王昊, 郭亮, 张庆茂. 聚碳酸酯红外激光抛光工艺的研究[J]. 应用激光, 2019, 39(3): 462. Xu Sizhi, Wang Hao, Guo Liang, Zhang Qingmao. Study on Infrared Laser Polishing Process of Polycarbonate[J]. APPLIED LASER, 2019, 39(3): 462.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!