Ba2YAlO5∶Eu3+, Na+荧光粉的合成和光致发光性能研究

Synthesis and Photoluminescence Properties of Ba2YAlO5∶Eu3+, Na+ Phosphor
作者单位
贵州大学大数据与信息工程学院,贵州省电子功能复合材料特色重点实验室,贵阳 550025
摘要
本文采用高温固相法成功合成了一系列Ba2YAlO5∶0.2Eu3+, xNa+(x=0.01,0.03,0.05,0.10,0.20,0.30)荧光粉,研究了Eu3+,Na+掺杂对晶体结构的影响。使用扫描电子显微镜观察荧光材料的微观形貌,使用荧光光谱仪对荧光粉的激发和发射光学特性进行观测和分析,从理论上研究了浓度猝灭和能量传递现象。在613 nm监测波段下,激发光谱在270~290 nm处出现O2-→Eu3+电荷转移带,395 nm和465 nm处出现峰值,在465 nm处峰值最大,对应于7F0→5D2跃迁。在465 nm监测波长下,观察到在613 nm处发射峰最强,对应于5D0→7F2跃迁,钠离子最优掺杂浓度为x=0.03。通过理论计算得出基质中的能量传递在最近邻离子之间。对发光材料进行热稳定性测试和分析,计算得到热猝灭激活能的值为0.058 eV,计算出Ba2YAlO5∶0.2Eu3+, 0.03 Na+荧光粉的色坐标位于(0.61, 0.39),非常接近于国际照明委员会规定的标准色坐标(0.67, 0.33)。
Abstract
A series of Ba2YAlO5∶0.2Eu3+, xNa+(x=0.01, 0.03, 0.05, 0.10, 0.20, 0.30) phosphors were synthesized successfully by high temperature solid phase method. The effect of Eu3+, Na+ doping on the crystal structure was studied. Observe the morphology of fluorescent materials with scanning electron microscope. The excitation and emission optical properties of phosphors were observed and analyzed by fluorescence spectrometer. Conducted theoretical research on concentration quenching and energy transfer. Under 613 nm emission, O2-→Eu3+ charge transfer band appears at 270 nm to 290 nm, peaks appear at 395 nm and 465 nm, the peak at 465 nm is the highest, corresponding to the 7F0→5D2 transition. Under 465 nm excitation, it is observed that emission peak is the strongest at 613 nm, corresponding to the 5D0→7F2 transition, and the optimal doping concentration of sodium ion is x=0.03. Theoretical calculation verified that the energy transfer in the host material is between the nearest neighbor ions. Thermal stability test analysis of the luminescent material show that activation energy of thermal quenching is 0.058 eV, and color coordinates of Ba2YAlO5∶0.2Eu3+, 0.03 Na+ phosphors are calculated locate in (0.61, 0.39), which is very close to the standard chromaticity coordinates (0.67, 0.33) stipulated by the International Commission on Lighting.

段欢, 崔瑞瑞, 邓朝勇. Ba2YAlO5∶Eu3+, Na+荧光粉的合成和光致发光性能研究[J]. 人工晶体学报, 2020, 49(12): 2302. DUAN Huan, CUI Ruirui, DENG Chaoyong. Synthesis and Photoluminescence Properties of Ba2YAlO5∶Eu3+, Na+ Phosphor[J]. Journal of Synthetic Crystals, 2020, 49(12): 2302.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!