现代显示, 2012, 23 (3): 18, 网络出版: 2012-03-30
显示器防护玻璃表面处理技术
Display Protective Glass Surface Treatment Technology
摘要
采用酸溶液湿法腐蚀和镀制增透、保护膜层的方法,对某型仪表用显示器防护玻璃表面进行了工艺处理,使得表面反射率降低到2%以下,产品可见光波段平均透过率达到86%,表面硬度提高到7.0GPa。产品性能检测和试用情况表明,防护玻璃具有较好的防眩、增透和抗划伤的作用,使用效果良好。
Abstract
Display protective glasses of a certain type instrument were technically processed by use of wet etching with acid solution and AR protective coating method. The reflectivity of surface was reduced to 2% below, the average transmittance of products was 86% in visible light, and the hardness of surface was enhanced to 7.0 GPa. The products' performance testing and trials expressed that, the protective glasses have good anti-glare, antireflective, scratch-resistant process and good behaviors.
参考文献
[1] 王承遇,潘玉昆,卢 琪等. 玻璃表面工程的进展[J]. 玻璃与搪瓷,2003,31(5):45-50.
[2] 吴春春,杨 辉,袁 骏等. 抗静电防眩膜研究进展[J]. 材料科学与工程,2002,20(1):133-135.
[3] 胡沛然,韩文爵,王海风等. Na2SiF6和ZnCl2对玻璃防眩光效果的影响研究[J]. 化工新型材料,2009,37(11):84-95.
[4] 唐晋发,顾培夫,刘 旭等. 现代光学薄膜技术[M]. 杭州:浙江大学出版社,2006.
[5] 罗春炼,韩文爵,王海风等. 提高防眩玻璃透过率的主要影响因素[J]. 化工新型材料,2008,36(12):89-91.
[6] 黄腾超,沈亦兵,陈海星等. 应用于MOEM S器件的K9玻璃湿法刻蚀工艺的研究[J]. 光学仪器,2004,26(2):151-155.
[7] 国防科学技术委员会. 中华人民共和国军用标准 光学膜层通用规范 GJB 2485-1995[B]. 中国标准出版社,1995.
王保松, 张国升, 谢钦. 显示器防护玻璃表面处理技术[J]. 现代显示, 2012, 23(3): 18. WANG Bao-song, ZHANG Guo-sheng, XIE Qin. Display Protective Glass Surface Treatment Technology[J]. ADVANCED DISPLAY, 2012, 23(3): 18.