红外与激光工程, 2020, 49 (12): 20201071, 网络出版: 2021-01-14
表面增强硫系玻璃Ge28Sb12Se60薄膜非线性吸收(特邀)
Surface enhanced nonlinear absorption of chalcogenide Ge28Sb12Se60 film (Invited)
图 & 表
图 2. Z -scan optical path for optical nonlinear refraction and nonlinear absorption measurement of samples
用于样品非线性折射与吸收测量的Z -scan光路
Fig. 2.
图 3. Open aperture Z -scan results obtained from experimental measurement and theoretically fitting. (a) GSS 20 nm only; (b) Ag 20 nm coated with GSS 20 nm; (c) Annealed Ag film coated with GSS 20 nm
开孔Z -scan实验测量与理论拟合结果。(a)只有GSS 20 nm;(b)银膜 20 nm加GSS 20 nm;(c)退火银结构加GSS 20 nm
Fig. 3.
图 4. Transmittance spectra of GSS 20 nm, annealed Ag, and annealed Ag with GSS 20 nmGSS 20 nm、退火银结构、退火银结构加GSS 20 nm三种样品的透过率谱
Fig. 4.
刘艺超, 周姚, 赵建行, 周见红, 宋瑛林. 表面增强硫系玻璃Ge28Sb12Se60薄膜非线性吸收(特邀)[J]. 红外与激光工程, 2020, 49(12): 20201071. Yichao Liu, Yao Zhou, Jianxing Zhao, Jianhong Zhou, Yinglin Song. Surface enhanced nonlinear absorption of chalcogenide Ge28Sb12Se60 film (Invited)[J]. Infrared and Laser Engineering, 2020, 49(12): 20201071.