远程荧光粉形状对LED发光性能的影响

研究了不同驱动电流和光强分布条件下, 圆顶形、椭球形以及圆锥形远程荧光粉的发光性能。实验采用蓝光LED激发YAG: Ce3+荧光粉产生白光, 并通过恒流源和TEC控温热沉分别控制LED驱动电流和热沉温度, 通过对三种不同形状远程封装的荧光粉的光、色指数等进行对比, 发现椭球状样品的综合光学特性最佳, 光通量最高。同时, 三种远程荧光粉分别进行了不同电流下的Yellow-blue Ratio (YBR) 空间分布测试, 结果显示, 圆顶形样品的YBR空间分布均匀性最好, 且在不同电流下ACCTD及ACU值在三种样品中最优。相比大角度, 三种样品在0°附近测量的YBR的值都有不同程度的下降, 原因是芯片法线方向的荧光粉离光源较远, 且光通过荧光粉的光程较短, 因此激发效果与大角度出光时有差别。光源的封装形状以及荧光粉形状都成为影响光分布的重要因素, 因此通过改变远程荧光粉的封装方式, 优化出射光线路径, 可以起到改善远程荧光粉发光性能的重要作用, 对完善大功率白光LED光学特性的研究具有较好的参考价值。

Abstract

The luminous performances of remote phosphor with domed, elliptical and conical shapes under various drive currents and light intensity distributions are researched. A blue LED is used as the light source to excite YAG:Ce3+ phosphor to emit white light. Meanwhile, constant-current sources and TEC heat sink controllers are used to control LED driving current and heat sink temperature respectively. Comparing the optical and chromatic parameters of three remote packing phosphor samples with different shapes, it is found that the elliptical sample has the best optical characteristics and the highest luminous flux. Yellow-blue ratio (YBR) spatial distribution tests of the three kinds of remote phosphor are performed respectively under different currents. The domed sample shows the best YBR spatial distribution uniformity, ACCTD and ACU value are the best among three samples. Comparing to big angle, the YBR values of the three samples measured closed to 0° decrease at different levels for the phosphor layer at the normal direction of the chip far away from the light source and shorter optical path in phosphor, so the excitation effect is different from that of the big angle exit light. Based on experimental phenomenon, shapes of light source encapsulation and phosphor layer become important factors to influence light distribution. Therefore, the exit light path is optimized through changing the packing way of the remote phosphor, which is important to improve remote phosphor illumination performances and has better reference to the research on high power white light LED optical performances.

参考文献

[1] ZHU Yi-ting, Narebdran Nadarajah. Optimizing the performance of Remote Phosphor LEDs[J]. J Light&Vis. Env, 2008, 32(2):115-119.

[2] CHUNG Shang-chao, HO Pei-chen, LI Dunru. Effect of chip spacing on light extraction for light-emitting diode array[J]. Opt Express, 2015, 23(11): A640-A649.

[3] CHEN Kuo-ju, CHEN Hsin-chun, SHIH Min-hsiung, et al. Enhanced luminous efficiency of WLEDs using a dual-layer structure of the remote phosphor package[J]. J. Lightwave Technol, 2013, 31(12): 1941-1945.

[4] HUANG Hsin-tao, HUANG Yi-pai, TSAI Chuang-chuang,et al. Plannar lighting system using array of blue LEDs to excite yellow remote phosphor film[J]. J Disp Technol, 2011, 7(1):44-51.

[5] Narendran N, GU Y, Freyssinier-Nova J P, et al. Extracting phosphor-scattered phosphors to improve white LED efficiency[J]. Phys Stat Sol, 2015, 202(6): R60-R61.

[6] KIM Jong Kyu, LUO Hong. Strongly enhanced phosphor efficiency in GaInN white light-emitting diodes using remote phosphor configuration and diffuse reflector cup[J]. Jpn J Appl Phys, 2005, 44(5L): L649.

[7] Keppens A, Denijs S, Wouters S, et al. Modelling the spatial colour distribution of phosphor-white high power light-emitting diodes[J]. SPIE, 2010, 77(17):77170J-1-77170J-10.

[8] 徐国芳, 饶海波, 余心梅, 等. 白光LED光斑均匀性的改进[J]. 发光学报, 2008, 29 (4): 707-712.

[9] SUN Ching-cherng, CHEN Ching-yi, CHEN Cheng-chien, et al. High uniformity in angular correlated-color-temperature distribution of white LEDs from 2800K to 6500K[J]. Opt Express, 2012, 20(6): 6622-6630.

[10] WANG Si-min, CHEN Xing, CHEN Ming-xiang, et al. Improvement in angular color uniformity of white light-emitting diodes using screen-printed multilayer phosphor-in-glass[J]. Appl Optics, 2014, 53(36): 8492-8498.

[11] LIU Zong-yuan, WANG Kai, LUO Xiao-bing, et al. Realization of high spatial color uniformity for white light-emitting diodes by remote hemispherical YAG: Ce phosphor film[C]//2010 Proceedings 60th Electronic Components and Technology Conference (ECTC), 2010: 1703-1707.

[12] KUO Hao-chung, HUNG Cheng-wei, CHEN Hsin-chu, et al. Patterned structure of remote phosphor for phosphor-converted white LEDs[J]. Opt Express, 2011, 19(104): A930-A936.

[13] LIU Zong-yuan, LIU Sheng, WANG Kai, et al. Studies on optical consistency of white LEDs affected by phosphor thickness and concentration using optical simulation[J]. IEEE Transactions on Components and Packaging Technologies, 2010, 33(4): 680-687.

[14] 刘志彬, 钱可元, 罗毅. 荧光粉层形状对白光LED空间色温均匀性的影响[J]. 半导体光电, 2012, 33(5): 651-655.

[15] 宋国, 缪建文, 施建珍, 等. 一种提高白光LED相关色温分布均匀性的方法[J]. 光电子·激光, 2010, 21(7): 983-987.

[16] CHEN Hsin-chu, CHEN Kuo-ju, LIN Chien-chung, et al. Improvement in uniformity of emission by ZrO2 nano-particles for white LEDs[J]. Nanotechnology, 2012, 23(26): 265201.

[17] SU Qiang, PEI Zhi-wu, CHI Li-sheng, et al. The yellow-to-blue intensity ratio (Y/B)of Dy3+ emission[J]. J Alloy Compd, 1993, 192(1): 25-27.

[18] CHEN Hai-wei, LUO Zhen-yue, ZHU Rui-dong, et al. Tuning the correlated color temperature of white LED with a guest-host liquid crystal[J]. Opt Express, 2015, 23(10): 13060-13068.

肖华, 郭自泉, 党思佳, 王阳夏, 肖俊, 史园. 远程荧光粉形状对LED发光性能的影响[J]. 光电技术应用, 2017, 32(1): 10. XIAO Hua, GUO Zi-quan, DANG Si-jia, WANG Yang-xia, XIAO Jun, SHI Yuan. Impact of Remote Phosphor Shape on LED Luminous Performance[J]. Electro-Optic Technology Application, 2017, 32(1): 10.

远程荧光粉形状对LED发光性能的影响

关于本站 Cookie 的使用提示

全站搜索

远程荧光粉形状对LED发光性能的影响

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索