扫描速度对激光熔覆NiCoCrAlY涂层组织及性能的影响 下载: 811次
Effect of Scanning Speed on Microstructure and Properties of Laser Cladding NiCoCrAlY Coating
1 中国民航大学航空工程学院, 天津 300300
2 中国民航大学工程技术训练中心, 天津 300300
图 & 表
图 1. NiCoCrAlY合金粉末形貌
Fig. 1. NiCoCrAlY alloy powder morphology
下载图片 查看原文
图 2. 激光熔覆实验示意图
Fig. 2. Schematic of laser cladding test
下载图片 查看原文
图 3. 单道NiCoCrAlY涂层宏观形貌及涂层横截面图。(a1)(b1) 4 mm/s;(a2)(b2) 8 mm/s;(a3)(b3) 12 mm/s;(a4)(b4) 16 mm/s
Fig. 3. Macroscopic morphology and cross section morphology of single NiCoCrAlY coating. (a1) (b1) 4 mm/s; (a2) (b2) 8 mm/s; (a3) (b3) 12 mm/s; (a4) (b4) 16 mm/s
下载图片 查看原文
图 4. 扫描速度对单道NiCoCrAlY涂层成形情况的影响规律。(a)涂层高度和宽度;(b)涂层稀释率
Fig. 4. Influence of scanning speed on the forming of single NiCoCrAlY coating. (a) Height and width of coating; (b) dilution rate of coating
下载图片 查看原文
图 5. 单道NiCoCrAlY涂层的微观组织。(a1)~(d1)近表层区域;(a2)~(d2)中间区域;(a3)~(d3)结合区域
Fig. 5. Microstructure of single NiCoCrAlY coating. (a1)-(d1) Areas near top zones; (a2)-(d2) center zones; (a3)-(d3) bonding zones
下载图片 查看原文
图 6. NiCoCrAlY涂层硬度
Fig. 6. NiCoCrAlY coating hardness
下载图片 查看原文
图 7. 摩擦系数变化曲线。(a) 4 mm/s;(b) 8 mm/s;(c) 12 mm/s;(d) 16 mm/s
Fig. 7. Friction coefficient variation curves. (a) 4 mm/s; (b) 8 mm/s; (c) 12 mm/s; (d) 16 mm/s
下载图片 查看原文
图 9. NiCoCrAlY涂层磨损痕迹的SEM形貌。(a) 4 mm/s;(b) 8 mm/s;(c) 12 mm/s;(d) 16 mm/s
Fig. 9. SEM micrographs of wear tracks of NiCoCrAlY coating. (a) 4 mm/s; (b) 8 mm/s; (c) 12 mm/s; (d) 16 mm/s
下载图片 查看原文
图 10. NiCoCrAlY涂层磨损轨迹。(a) 3D轮廓图;(b)磨损截面深度曲线
Fig. 10. Wear tracks of NiCoCrAlY coating。(a) 3D profile; (b) depth curves of wear cross section
下载图片 查看原文
表 1NiCoCrAlY合金粉末化学成分
Table1. Chemical composition of NiCoCrAlY alloy powder
Element | Y2O3 | Co | Al | Cr | Ni |
---|
Mass fraction /% | Technical requirement | 0.5-0.8 | 2.2-2.8 | 4-6 | 15.5-17.5 | Balance | | Detection result | 0.58 | 2.46 | 4.52 | 16.94 | Balance |
|
查看原文
表 2IN718合金化学成分
Table2. Chemical composition of IN718 alloy
Element | C | Si | Mn | P | S | Cr | Ni | Cu | Mo | Ti | Co | Al | Nb+Ta | Fe |
---|
Mass fraction /% | 0.065 | 0.18 | 0.19 | 0.009 | 0.01 | 19.48 | 52.7 | 0.05 | 3.02 | 1.06 | 0.15 | 0.56 | 5.08 | Balance |
|
查看原文
表 3四种扫描速度下的NiCoCrAlY涂层主要元素含量
Table3. Contents of main elements of NiCoCrAlY coatings at four scanning speeds
Number | V /(mm·s-1) | Mass fraction /% |
---|
Ni | Co | Cr | Al | Fe |
---|
| 4 | 65.74 | 1.43 | 18.16 | 2.48 | 7.61 | 1 | 8 | 64.02 | 1.28 | 18.97 | 2.55 | 7.48 | | 12 | 64.49 | 1.24 | 18.49 | 2.71 | 7.54 | | 16 | 65.19 | 1.33 | 19.29 | 2.58 | 7.32 | | 4 | 64.87 | 1.33 | 19.47 | 3.77 | 7.68 | 2 | 8 | 64.62 | 1.27 | 18.96 | 3.56 | 8.25 | | 12 | 63.88 | 1.18 | 19.12 | 3.18 | 8.53 | | 16 | 63.02 | 1.43 | 18.91 | 3.12 | 8.32 | | 4 | 65.16 | 1.53 | 19.16 | 2.53 | 9.76 | 3 | 8 | 63.83 | 1.28 | 19.07 | 2.89 | 10.49 | | 12 | 65.42 | 1.14 | 19.53 | 2.67 | 9.37 | | 16 | 62.87 | 1.33 | 19.47 | 2.77 | 10.41 |
|
查看原文
王涛, 乔伟林, 王宁, 张金, 唐杰, 王浩, 吴军. 扫描速度对激光熔覆NiCoCrAlY涂层组织及性能的影响[J]. 激光与光电子学进展, 2020, 57(21): 211403. Wang Tao, Qiao Weilin, Wang Ning, Zhang Jin, Tang Jie, Wang Hao, Wu Jun. Effect of Scanning Speed on Microstructure and Properties of Laser Cladding NiCoCrAlY Coating[J]. Laser & Optoelectronics Progress, 2020, 57(21): 211403.