Emerging photoluminescence from defective vanadium diselenide nanosheets Download: 921次
Figures & Tables
Fig. 1. Schematic representation of VSe 2 NP and NS formation using the PLA and ultra-sonication-assisted chemical exfoliation.
Fig. 2. TEM images showing the successful formation of (a) laser-ablated NPs and (b) chemically exfoliated NSs. (c) HRTEM image showing the lattice spacing in the synthesized NSs. (d) SEM image of the drop-casted NS solution. (e) AFM measurement results showing the formation of single to a few layers of VSe 2 and its thickness profile.
Fig. 4. (a) Absorption spectra of the synthesized colloidal NPs and NSs. The inset estimates the optical band gap of the samples. (b) The transition from 1T phase to 2H phase in IR radiated VSe 2 samples.
Fig. 5. (a) Images of the NP and NS solutions before and after excitation with UV-incident light and (b) their PL spectra upon excitation with a 300 nm light. (c) The change of the emission spectra of the NS sample under different excitation wavelengths. (d) PL spectra change after irradiation with continuous light for 4 h. (e) The dependence of PL on the excitation light intensity at an excitation wavelength of 330 nm with different slit width values.
Amir Ghobadi, Turkan Gamze Ulusoy Ghobadi, Ali Kemal Okyay, Ekmel Ozbay. Emerging photoluminescence from defective vanadium diselenide nanosheets[J]. Photonics Research, 2018, 6(4): 04000244.