激光选区熔化成形2Cr13不锈钢组织与力学性能研究

刘正武; 朱小刚; 孙靖; 程灵钰; 赵维刚

doi:doi:10.14128/j.cnki.al.20193903.411

应用激光, 2019, 39 (3): 411, 网络出版: 2019-08-07

激光选区熔化成形2Cr13不锈钢组织与力学性能研究

Microstructure and Mechanical Properties of 2Cr13 Stainless Steel Using Selective Laser Melting

论文大纲

刘正武 ^*朱小刚孙靖程灵钰赵维刚

作者单位

上海航天设备制造总厂有限公司, 上海 200245

激光选区熔化成形 2Cr13不锈钢工艺参数显微组织力学性能 selective laser melting 2Cr13 stainless steel parameters microstructure mechanical properties

摘要

对2Cr13不锈钢粉末进行激光选区熔化成形研究, 开发成形工艺参数, 研究不同工艺参数下熔池凝固行为, 制备显微组织观察试块及力学性能测试试块, 观察成形件显微组织特征并测试成形件布氏硬度、弯曲强度、室温拉伸性能。结果显示, 当成形工艺参数为激光功率200 W、层厚30 μm、光点间距75 μm、曝光时间110 μs、线间距115 μm时, 成形件致密度达99.75%; 显微组织无孔洞, 成形件纵截面熔池搭接形成鱼鳞状形貌; 成形件强度高、塑性差且力学性能表现出各项异性, 横向性能与锻件相近, 纵向性能较弱。

Abstract

This work studies selective laser melting of 2Cr13 stainless steel. The main contents include the development of forming process parameters and the solidification behavior of molten pool under different process parameters. Besides, the microstructure observation test blocks are prepared and observed, mechanical property test blocks are prepared and tested, including Brinell Hardness, bending strength and room temperature tensile properties. The results show that when the forming process parameters are set as laser power 200 W, layer thickness 30 μm, spot spacing 75 μm, exposure time 110 μs, line spacing 115 μm, the density of the molded part reaches 99.75%. There is no hole in the formed part and the longitudinal section is lapped in the form of fish scales. The deposited parts have high strength, but the plasticity is poor and the performance shows an anisotropy. The lateral performance is similar to that of the forging but the longitudinal performance is weaker.

参考文献

[1] 杨永强, 吴伟辉, 来克娴, 等.金属零件选区激光熔化直接快速成形工艺及最新进展［J］.航空制造技术, 2006(2)：73-76.

YANG YONGQIANG, WU WEIHUI, LAI KEXIAN, et al.Newest progress of direct rapid prototyping of metal part by selective laser melting［J］.Aviation Manufacturing Technology, 2006(2)：73-76.

[2] 吴伟辉, 杨永强.选区激光熔化快速成形系统的关键技术［J］.机械工程学报, 2007, 43(8)：175-180.

WU WEIHUI, YAN YONGQIANG.Key technologies of selective laser melting rapid prototyping system［J］.Journal of Mechanical Engineering, 2007, 43(8)：175-180.

[3] READ N, WANG W, ESSA K, et al.Selective laser melting of AlSi10Mg alloy：Process optimisation and mechanical properties development［J］.Materials & Design, 2015(65)：417-424.

[4] WEINGARTEN C, BUCHBINDER D, PIRCH N, et al.Formation and reduction of hydrogen porosity during selective laser melting of AlSi10Mg［J］.Journal of Materials Processing Technology, 2015(221)：112-120.

[5] YASA E, KRUTH J P.Microstructural investigation of Selective Laser Melting 316L stainless steel parts exposed to laser re-melting［J］.Procedia Engineering, 2011, 19(1)：389-395.

[6] 李洋, 陈长军, 王晓南, 等.选区激光熔化技术制备316L多孔不锈钢工艺及性能研究［J］. 应用激光, 2015, 35(3)：319-323.

LI YANG, CHEN CHANGJUN, WANG XIAONAN, et al.Preparation and properties of 316L porous stainless steel by selective laser melting technology［J］.Applied Laser, 2015, 35(3)：319-323.

[7] ZHANG S, GUI R, WEI Q, et al.Cracking behavior and formation mechanism of TC4 alloy formed by selective laser melting［J］.Journal of Mechanical Engineering, 2013, 49(23)：21-27.

[8] MUMTAZ K, HOPKINSON N.Top surface and side roughness of Inconel 625 parts processed using selective laser melting［J］.Rapid Prototyping Journal, 2009, 15(2)：96-103.

[9] 王平怀, 王伯健, 宋景娜.淬火温度对2Cr13不锈钢组织和性能的影响［J］.热加工工艺, 2008, 37(4)：71-73.

WANG PINGHUAI, WANG BOJIAN, SONG JINGNA.Effect of quenching temperature on microstructure and properties of 2Cr13 stainless steel［J］.Thermal Process Technology, 2008, 37(4)：71-73.

[10] 张学军, 唐思熠, 肇恒跃, 等.3D打印技术研究现状和关键技术［J］.材料工程, 2016, 44(2)：122-128.

ZHANG XUEJUN, TANG SIYI, ZHAO HENGYUE, et al.Research status and key technologies of 3D printing technology［J］.Journal of Materials Engineering, 2016, 44(2)：122-128.

刘正武, 朱小刚, 孙靖, 程灵钰, 赵维刚. 激光选区熔化成形2Cr13不锈钢组织与力学性能研究[J]. 应用激光, 2019, 39(3): 411. Liu Zhengwu, Zhu Xiaogang, Sun Jing, Cheng Lingyu, Zhao Weigang. Microstructure and Mechanical Properties of 2Cr13 Stainless Steel Using Selective Laser Melting[J]. APPLIED LASER, 2019, 39(3): 411.

激光选区熔化成形2Cr13不锈钢组织与力学性能研究

关于本站 Cookie 的使用提示

全站搜索

激光选区熔化成形2Cr13不锈钢组织与力学性能研究

相关论文

相关资讯

关于本站 Cookie 的使用提示

全站搜索